| Product name | Product index | Purpose | Characteristic | |||
| Acid value（mgKOH/g） | Softening(℃) | Color (Gardner) | ||||
| Polyol modified resin | AS-2100D | ≦5 | 96-102 | ≦7 | Acrylic adhesive, rubber adhesive, hot melt adhesive | Good heat resistance and enhanced initial adhesion |
| AS-2125D | ≦18 | 120-130 | ≦9 | Acrylic adhesive, rubber adhesive, hot melt adhesive | Good heat resistance, stable color | |
| AS-1100G | 2.5-4.2 | 95-102 | ≦5 | Acrylic adhesive, rubber adhesive, hot melt adhesive | Low odor, enhanced initial viscosity | |
| AS-1120G | ≦35 | 115-125 | ≦8 | Acrylic adhesive, rubber adhesive, hot melt adhesive | High acid value, high softening point | |
| AS-1050G | ≦18 | 3500-5000 (mPa.s, 60℃) | ≦7 | Rubber adhesive, acrylic adhesive | Liquid resin, good initial adhesion at low temperature | |
| AS-3120P | 12-14 | 118-128 | ≦11 | Acrylic adhesive, rubber adhesive, hot melt adhesive | High temperature resistance, good film adhesion | |
| AS-3130P | 8-13 | 128-138 | ≦10 | Acrylic adhesive, rubber adhesive, hot melt adhesive | High temperature resistance, good film adhesion | |
| AS-3140P | ≦20 | 140-150 | ≦12 | Acrylic adhesive, rubber adhesive, hot melt adhesive | High temperature resistance, good film adhesion | |
| AS-3165P | ≦20 | 165-175 | ≦12 | Acrylic adhesive, gravure ink | High temperature resistance, good film adhesion | |
| AS-1102G | 6-12 | 98-106 | ≦10 | Rubber adhesive, rubber modifier (for tire) | Friction resistance, good viscosity | |
| AS-1105M | ≦25 | 100-110 | ≦7 | Acrylic adhesive, UV ink | Good stickiness | |
| AS-1105A | 15-25 | 105-115 | ≦9 | Acrylic adhesive, rubber adhesive, hot melt adhesive | Film adhesion is good | |
| WR7110 | ≦16 | 95-105 | ≦5 | Acrylic adhesive, hot melt adhesive | Light color, good aging resistance | |
| WR0095 | ≦30 | 85-95 | ≦1 | Acrylic adhesive, hot melt adhesive | Light color, good aging resistance | |